About the product
Get to know Aidite 3D pro zir
Material Composition & Physical Properties
- Zirconia Content (ZrO2): "Ranges from 90% to 95%."
- Yttria Content (Y2O3): "Ranges from 4% to 10%."
- Alumina Content (Al2O3): "Less than or equal to 0.5%."
- Other Oxides: "Less than 0.5%."
- Sintered Density: "Greater than or equal to 6.0 g/cm³."
- Coefficient of Thermal Expansion K⁻¹ (25~500°C): "Approximately (10.5 ± 1.0) x 10⁻⁶."
- Surface Monoclinic Phase Content After Accelerated Aging: "Less than 5%."
- Chemical Solubility: "Less than 100 µg/cm²."
Strength and Translucency
- Fabrication Process: "Fabricated using advanced production processes to achieve a layerless, natural shade gradient."
- Flexural Strength: "Exhibits a 3-point test flexural strength of greater than 1050 MPa."
- Gradient Transition: "Optimizes strength and translucency, transitioning smoothly from cervical to incisal areas of the restoration."
- Layer Specific Properties: Incisal Layer: "700 MPa flexural strength and 57% translucency." Cervical Layer: "1050 MPa flexural strength and 43% translucency."
- Aesthetic Outcome: "Ensures highly aesthetic results suitable for various dental indications."
Indications for Use & Preparation Guidelines
- Indications: "Suitable for a wide range of indications, from single crowns to 14-unit bridge structures." "Includes veneers, inlays, anterior and posterior crowns, full arch crown bridges, full contour screw retained bridges, and implant-supported restorations."
- Recommended Preparation Dimensions (Examples):
- Axial Wall Thickness (Crown): "Anterior: ≥0.7 mm, Posterior: ≥0.8 mm."
- Occlusal Thickness (Crown & Bridge): "≥1.0 mm for both anterior and posterior."
- Bridge Connectors (Anterior): "For up to 3 units: ≥9 mm²; for 4 units and above: ≥9 mm²."
- Bridge Connectors (Posterior): "For up to 3 units: ≥12 mm²; for 4 units and above: ≥20 mm²."
Sintering Cycles & Digital Workflow
- Sintering Capabilities: "The 3D Pro zir range supports fast, high-performance sintering (e.g., a 2-hour cycle for single units and bridges up to 3 units) as well as more conventional cycles for larger spans." "This flexibility enables shorter production times, reduced costs, and faster delivery."
- Fast Sintering Cycle (2-hour for single units & 1-3 unit bridges):
- Start Temperature: "20°C."
- Phase 1 Heating Rate: "52°C/min up to 1200°C."
- Phase 2 Heating Rate: "6°C/min up to 1550°C (with a 30-minute hold time)."
- Cooling Rate: "55°C/min down to 900°C."
- Digital Workflow Integration: "The material is an integral part of an entire validated digital workflow, from initial intraoral scan to the final restoration." "Workflow components include Intraoral Scanner, Design (e.g., exocad), Milling (e.g., AMD-500DCS), Fast Sintering (e.g., CSF-200s), and Glazing (e.g., Biomic Stain/Glaze)."
- o Customization Note: "Firing temperatures and times are guidelines and may require adjustment based on the specific sintering furnace's condition and calibration."
Available Shades & Dimensions
- Shade Range: "Available in 16 shades from the classical VITA® shade guide and 3 bleach shades (OM1, OM2, OM3)." "Additional popular shades from the VITA® 3D master shade guide (1M1, 4M2, 4M3, 5M1, 5M2, 5M3) are also available."
- Custom Characterization: "Biomic Stain&Glaze can be used for individual further characterization to achieve highly aesthetic results."
- Disc/Block Heights: "Available in various heights (e.g., 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm) to suit different system requirements."
- Disc System Compatibility: "Supports Standard open systems (D98*), Girrbach systems (AG71*), and Zirkonzahn systems (D95*)."
- Chairside Block Options: "Available for Sirona systems in sizes such as 201514, 201519, 401514, 401519, 5515.519, and 652522." "Other chairside block sizes can be customized to meet special requirements."
Brand or manufacturer
Meet Qasr Al-Tibb Medical Partners
Aidite (Qinhuangdao) Technology Co., Ltd.
Aidite (Qinhuangdao) Technology Co., Ltd. is a leading Chinese manufacturer specializing in advanced dental materials and solutions. Established in 2007, the company has gained global recognition for its high-quality zirconia blocks, CAD/CAM milling machines, and digital dentistry systems. With a focus on innovation, precision, and biocompatibility, Aidite provides reliable products that support modern restorative and prosthetic dentistry. Its strong commitment to research, development, and international standards has made Aidite a trusted partner for dental professionals worldwide, offering solutions that enhance efficiency, aesthetics, and patient care.